Quality control
1. Quality is the life, YUCERA is confident in the superior quality
of products being the most effective salesman.
2. YUCERA has advanced production management and R & D technology
and also continue to technical innovations.
3. YUCERA introduces new industrial automation equipment, and
gradually optimize the every aspect of production process.
4. YUCERA brings in advanced quality test equipments so as to
control all laser machines.
5. YUCERA has its own complete set of test methods and test
standard.
Super translucent zirconia blocks
zirconia blocksare made of nanometer medical grade zirconia powder.
The powder are firstly compacted by cold isostaticpressing with
high compressive strength and then pre-sintered to a certain degree
to offer good machinability.
ST zirconia blocks can be used to create crowns, bridges, inlays
and veneers of fixed partial denture with different translucency
levels and colors.
Product Features
Safety:No irritation,No corrosion,Good bio-compatibility
Beauty:Natural teeth color can be reproduced
Comfortability:Low thermal conductivity,hot and cold changes do not
stimulte the pulp
Durability:Over 1600MPa perturbed strength, durable and useful
HT/ST Sintering Curve (1-5)
HT/ST Sintering Curve (1-5) |
Sintering step | Start Temperature(℃) | End Temperature(℃) | Time(Min) | Rate(℃/Min) |
Step 1 | 20 | 300 | 30 | 9.3 |
Step 2 | 300 | 1200 | 150 | 6 |
Step 3 | 1200 | 1530 | 110 | 3 |
Step 4 | 1530 | 1530 | 120 | 0 |
Step 5 | 1530 | 800 | 100 | -7.3 |
Step 6 | 800 | natural cooling 20 | 120 | -6.5 |
HT/ST Sintering Curve (10 units)
HT/ST Sintering Curve (10 units) |
Sintering step | Start Temperature(℃) | End Temperature(℃) | Time(Min) | Rate(℃/Min) |
Step 1 | 20 | 300 | 30 | 9.3 |
Step 2 | 300 | 1200 | 190 | 4.7 |
Step 3 | 1200 | 1530 | 150 | 2.2 |
Step 4 | 1530 | 1530 | 120 | 0 |
Step 5 | 1530 | 800 | 120 | -6 |
Step 6 | 800 | natural cooling 20 | 120 | -6.5
|
ST Color Zirconia Block
*Pre-shaded technics
*Uniform color
*Without post dyeing posses
*Suitable for full contour crown, bridge and anterior
Indications
Crown, Inlay, Onlay, 2-5 unit Bridges, Anterior
Physical Characteristics
Physical Characteristics |
Sintered density 6.07±0.01g/cm³ |
Bending Strength 1200 MPa |
Transmittance 43% |
Hardness 1200HV |
Sintering temperature 1480~1550℃/recommend 1530℃ |